0040AA:
day 0
p2: 3 to -3 V 61 samples, 5 to -5 V 101 samples, 10 to -10 V 101 samples
p3: 1 measurement point at like 3000 mA/cm2 at 10 V and then straight to zero, probably burnt
p4: 5 to -5 V 101 samples
p5: 3 to -3 V 61 samples
p6: 3 to -3 V 61 samples
p7: 5 to -5 V 101 samples
p8: 10 to -10 V 101 samples, some e-5 at 9-10 V and then into e-6 negatives even at positive V, then goes into e-5 negative at -10 V so something works

- p2 looked burnt afterwards

0040A5:
day 1
p2: 3 to -3 V 61 samples, 5 to -5 V 101 samples, 10 to -10 V 101 samples
p3: 10 to -10 V 101 samples
p4: 5 to -5 V 101 samples
p5: 3 to -3 V 61 samples
p6: 3 to -3 V 61 samples
p7: 5 to -5 V 101 samples
p8: 10 to -10 V 101 samples

0040A6:
day1
p2: 3 to -3 V 61 samples, 5 to -5 V 101 samples, 10 to -10 V 101 samples
p3: 10 to -10 V 101 samples
p4: 5 to -5 V 101 samples
p5: 3 to -3 V 61 samples
p6: 3 to -3 V 61 samples
p7: 5 to -5 V 101 samples
p8: 10 to -10 V 101 samples

0040A7:
day 1
p2: 3 to -3 V 61 samples, 5 to -5 V 101 samples, 10 to -10 V 101 samples
p3: 10 to -10 V 101 samples
p4: 5 to -5 V 101 samples
p5: 3 to -3 V 61 samples
p6: 3 to -3 V 61 samples
p7: 5 to -5 V 101 samples
p8: 10 to -10 V 101 samples

0040A8:
day 1
p2: 3 to -3 V 61 samples, 5 to -5 V 101 samples, 10 to -10 V 101 samples
p3: 10 to -10 V 101 samples
p4: 5 to -5 V 101 samples
p5: 3 to -3 V 61 samples
p6: 3 to -3 V 61 samples
p7: 5 to -5 V 101 samples
p8: 10 to -10 V 101 samples

0040A9:
day 1
p2: 3 to -3 V 61 samples, 5 to -5 V 101 samples, 10 to -10 V 101 samples
p3: 10 to -10 V 101 samples
p4: 5 to -5 V 101 samples, 3 to -3 V 61 samples
p5: 3 to -3 V 61 samples
p6: 5 to -5 V 101 samples
p7: 3 to -3 V 61 samples
p8: 10 to -10 V 101 samples